mag3D  Figure1 Figure2   Figure3  PRESENTATION SYMPOSIUM FRANCO FINLANDAIS  SYMPOSIUM  Problème des phases The phase problem  DVD Semi-conducteur organométallique  organosilicié TiO2-rutile  SiO2-stishovite  Cu2O-cuprite  K2PtCl6 Be-metal  bases and 3D views Bases et vues 3D Si-et-Ge  CaF2-fluorite  NbC-2023

 

 

 

 

 

 

 

Indications of Magnetic State in the Charge Distributions in MnO, CoO and NiO.

I : Para- and Antiferromagnetism of MnO 

          

Jean-Pierre Vidal, Geneviève Vidal –Valat

Laboratoire d’Analyse Multipolaire des Répartitions de Charges Expérimentales, cc26,

Université Montpellier 2, 34095 Montpellier, Cedex 05, France

e-mail : genevieve.vidal@umontpellier.fr     jpvidal34@orange.fr

 

Kaarle Kurki-Suonio  Physics Department, P.O. Box 64, FIN-00014 University of Helsinki, Finland

 

Kristallografiya, 2002, Vol. 4, N°3, pp. 391-405.( in russian )

Crystallographic Reports, 2002, Vol. 47, N°3, pp. 347-361.( in english )

 

 

Fig. 5 Three-dimensional view on the equivalue surfaces of  the ionic multipole expansions.

Surface-representations +0.1 and − 0.1 eÅ−3 and

section-representations + 0.25 to − 0.25 eÅ−3,

the zero value is omitted. Contours are spaced by 0.05 eÅ−3.

   (a) the paramagnetic state (298K)               (b) the antiferromagnetic state (85K)
 

 

 

Autres vues complémentaires en demi-volume même orientation.

Rs = rayon de la sphère sur laquelle sont tracées des isolignes.

Ri = rayon de la sphère pour l’isosurface 0,1e/Å3.

Re = rayon de la sphère d’exploration.

 

 

 

 

   

 

 

 

mag3D  Figure1 Figure2   Figure3  PRESENTATION SYMPOSIUM FRANCO FINLANDAIS  SYMPOSIUM  Problème des phases The phase problem  DVD Semi-conducteur organométallique  organosilicié TiO2-rutile  SiO2-stishovite  Cu2O-cuprite  K2PtCl6 Be-metal  bases and 3D views Bases et vues 3D Si-et-Ge  CaF2-fluorite  NbC-2023